Role of microadditives in activation of self–extending hightemperature synthesis of systems on the basis of the silicon dioxide
Abstract
Laws of initiation and burning of system SiO2+Al in the conditions of activation of reaction of burning by additives of the various organic connections containing bonding water and amino groups are investigated. It is shown that at introduction of additives in an initial mix the induction period of ignition, cinetics of burning and thermodynamic characteristics of process that promotes fuller development of oxidation–reduction reactions and formation of ultradisperse nitride compounds promoting hardening of the synthesized sample.
References
2. Мержанов А.Г. Процессы горения и взрыва в физикохимии и технологии неорганических материалов // Успехи химии. – 2003. – Т.72, №4. – С.323 – 345.
3. Ляхов Н.З., талако Т.Л.. Григорьева Т.Ф. Влияние механоактивации на процессы фазо– и структурообразования при самораспространяющемся высокотемпературном синтезе. – Новосибирск: Параллель, 2008 – C.168.
4. Мофа Н.Н. Композиционные материалы, полученные СВ–синтезом предварительно активированного и модифицированного кварцсодержащего материала // Труды Всероссийской конференции «Процессы горения и взрыва в физиикохимии и технологии неорганических материалов» – М., 2002. – С.278 – 282.
5. Абовян Л.С., Нерсисян Г.А., Харатян С.Л. Активированное горение системы SiO2 – Al–C и синтез композиционных порошков SiC/Al2O3 // Физика горения и взрыва. 2000. Т. 36, №2. – С.51 –55.
Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License (CC BY-NC-ND 4.0) that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.